<noframes id="b9j9x">
<sub id="b9j9x"></sub>
<sub id="b9j9x"></sub>
<sub id="b9j9x"></sub>
<address id="b9j9x"><address id="b9j9x"></address></address>

    <address id="b9j9x"></address><noframes id="b9j9x"><address id="b9j9x"><listing id="b9j9x"></listing></address>

    <address id="b9j9x"><listing id="b9j9x"><menuitem id="b9j9x"></menuitem></listing></address>

      您好!欢迎访问东莞市恒科自动化设备有限公司的官方网站!

      恒科产品分类

      Product Categories
      4造纸行业国家标准文库ASTM 标准汇总
      您的位置: 首页 -> 造纸行业国家标准文库 ->  ASTM 标准汇总 -> ASTM D4798–01 免费下载

      ASTM D4798–01 免费下载


      Designation: D 4798 – 01

      Standard Practice for

      Accelerated Weathering Test Conditions and Procedures for

      Bituminous Materials (Xenon-Arc Method)1

      This standard is issued under the fixed designation D 4798; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reaproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.

      1. Scope

      1.1 This test method covers test conditions and procedures

      for xenon-arc exposures according to Practices G 151 and

      G 155 for bituminous roofing and waterproofing materials that

      have a minimum softening point of approximately 95°C

      (200°F) as determined by Test Method D 36. (Also see

      Terminology G 113.)

      1.2 The values stated in SI units are to be regarded as the

      standard. The values given in parentheses are for information

      only.

      1.3 This standard does not purport to address all of the

      safety concerns, if any, associated with its use. It is the

      responsibility of the user of this standard to establish appropriate

      safety and health practices and determine the applicability

      of regulatory limitations prior to use.

      2. Referenced Documents

      2.1 ASTM Standards:

      D 36 Test Method for Softening Point of Bitumen (Ringand-Ball Apparatus)2

      D 1669 Practice for Preparation of Test Panels for Accelerated

      and Outdoor Weathering of Bituminous Coatings2

      D 1670 Test Method for Failure End Point in Accelerated

      and Outdoor Weathering of Bituminous Materials2

      G 113 Terminology Relating to Natural and Artificial

      Weathering Tests of Nonmetallic Materials3

      G 141 Guide for Addressing Variability in Exposure Testing

      on Nonmetallic Materials3

      G 147 Practice for Conditioning and Handling of Nonmetallic

      Materials for Natural and Artificial Weathering Tests3

      G 151 Practice for Exposing Nonmetallic Materials in Accelerated

      Test Devices that Use Laboratory Light Sources3

      G 155 Practice for Operating Xenon Arc Light Apparatus

      for Exposure of Nonmetallic Materials3

      3. Summary of Test Method

      3.1 Thin films of bitumen are uniformly applied to aluminum

      panels. Shingles and similar products are cut to size and

      exposed to specified cycles of temperature, light, and water. A

      choice of two test cycles is given along with options for

      determining the period of exposure and evaluating results.

      4. Significance and Use

      4.1 It is not possible to establish a precise correlation

      between accelerated and natural weathering because of geographical

      climatic variations, local weather variation from

      normal, and local pollutants. This weathering apparatus and

      procedure are used for comparing the weathering characteristics

      of bituminous materials against a reference material for

      which the outdoor weathering characteristics are known. Guide

      G 141 provides guidance regarding this issue.

      5. Apparatus

      5.1 The xenon-arc apparatus used shall conform to the

      requirements defined in Practices G 151 and G 155.

      5.2 Filters—Daylight filter as described in Practice G 155.

      5.3 Radiometer—The use of a radiometer to monitor and

      control the amount of radiant energy received at the specimen

      is required. The use of the radiometer shall comply with the

      requirements in Practice G 151.

      6. Test Specimens

      6.1 Unless otherwise agreed upon, test specimens shall be

      approximately 70 by 150 mm (23by 57in.). Bituminous

      materials shall be applied as uniform coatings on aluminum

      panels in accordance with Practice D 1669. Fabricated materials

      such as bituminous roofing, shingles, and similar products

      shall be cut to size and their weather surfaces exposed. If these

      are too flexible to sustain their own weight in a vertical

      position, they may be mounted on aluminum panels.

      6.1.1 Unless otherwise specified, expose at least three replicate

      specimens of each test and control material.

      6.1.2 Other test specimen sizes may be used to provide

      sufficient material for postexposure testing when desired.

      6.1.3 Follow the procedures described in Practice G 147 for

      identification, conditioning, and handling of specimens of test,

      control, and reference materials before, during, and after

      exposure.

      6.1.4 Do not mask the face of a specimen for the purpose of

      showing on one panel the effects of various exposure times.

      Misleading results may be obtained by this method, since the

      masked portion of the specimen is still exposed to temperature

      and humidity cycles that in many cases will affect results.

      7. Procedure

      7.1 Proceed in accordance with Section 9 of Practice G 155.

      7.2 Water Purity:

      7.2.1 The purity of water used for specimen spray is very

      important.Without proper treatment to remove cations, anions,

      organics, and particularly silica, exposed panels will develop

      spots or stains that may not occur in exterior exposures.

      7.2.2 Follow the requirements for water purity described in

      Practice G 151.

      7.2.3 If specimens are found to have deposits or stains after

      exposure in the apparatus, the water purity must be checked to

      determine if it meets the requirements of 7.2.2. On some

      occasions, exposed specimens can be contaminated by deposits

      from bacteria that can grow in the purified water used for

      specimen spray. If bacterial contamination is detected, the

      entire system used for specimen water spray must be flushed

      with chlorine and thoroughly rinsed before resuming exposures.

      7.2.4 The temperature of water used for specimen spray

      shall be 7.2 3°C (45 5°F).

      7.2.5 When the water purity requirements above are met and

      there is disagreement between parties on the extent of problems

      caused by stain or deposit, run referee tests in at least one other

      laboratory that can meet the water quality requirements described

      in 7.2.

      7.3 Unless otherwise specified, operate the apparatus continuously

      according to one of the following schedules for 24 h

      at a light intensity of 0.35 W/mat 340 nm.

      7.3.1 Cycle A—51-min light exposure, 9-min light and

      water spray; black panel temperature (60 3°C).

      7.3.2 Cycle B—60-min water spray, 90-min light exposure,

      120-min water spray, 990-min light exposure, 180-min cold

      exposure; black panel temperature (60 3°C).

      7.3.3 The 24-h cycle requires automatic control of the

      periods of light and light with spray.

      7.3.4 For the cold exposure period in Cycle B, the panels

      shall be placed in the refrigerator, previously cooled to −18 6

      5°C (0 10°F). If inspection of the panels is to be performed

      at any stage in the cycle or sequence of cycles, the interruption

      of the test procedure should take only sufficient time to allow

      for such inspection. When inspection of the panels is not

      performed, the transfer of the panels from the exposure

      apparatus to the refrigerator, and following this period, back to

      the test chamber, shall not require more than 15 min.

      7.3.5 The time taken for inspection of the panels shall not be

      counted as part of the 24-h exposure cycle.

      8. Period of Exposure and Evaluation of Test Results

      8.1 The duration of the exposure under this test method

      shall be one of the following:

      8.1.1 A mutually agreed upon number of 24-h cycles of

      operation in accordance with either Cycle A or Cycle B,

      8.1.2 The number of 24-h cycles required to produce a

      mutually agreed upon minimum amount of change in the test

      specimen, or

      8.1.3 The number of 24-h cycles required to produce

      mutually agreed upon minimum acceptable changes in either

      the test specimen or a mutually agreed upon reference sample.

      8.2 Changes in the exposed specimens may be evaluated

      visually at the end of each 24-h cycle by comparing them with

      unexposed samples, or in terms of the number of cycles

      required to produce physical or chemical changes as determined

      by Test Method D 1670.

      9. Report

      9.1 In addition to the items specified in Practice G 151, the

      report shall include the following information:

      9.1.1 Cycle used (refer to this test method),

      9.1.2 Level of irradiation used,

      9.1.3 Coating thickness used, and

      9.1.4 Method of sample rotation used.

      10. Precision and Bias

      10.1 Precision—The repeatability of results obtained in exposures conducted according to this practice will vary with the materials being tested, the material property being measured,and the specific test conditions and cycles that are used.It is essential to determine reproducibility of the exposure/property measurement process when using the results from exposures conducted according to this practice in product specifications.

      10.2 Bias—Bias cannot be determined because no acceptable

      standard weathering reference materials are available.

      11. Keywords

      11.1 accelerated weathering; bituminous materials; degradation;exposure; light exposure; roofing;ultraviolet; waterproofing;xenon-arc

      ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned

      in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk

      of infringement of such rights, are entirely their own responsibility.

      This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and

      if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards

      and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the

      responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should

      make your views known to the ASTM Committee on Standards, at the address shown below.

      This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,

      United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above

      address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website